Ftir analysis laboratories with MicroVision Laboratories, Inc. today? The scan from left to right shows a high tin concentration (green line) while areas of higher lead concentrations (blue line) were not intersected by the line scan. At the interface between the tin/lead solder and copper (red line), there is a mixture of the solder and copper which is the intermetallic layer. The EDS Map provides a nice visual mixture of colors which shows the intermetallic layer while the line scan clearly shows the intermetallic with the elemental graph.
Problem: A client was a manufacturer of beverages, bottled water, and other drinks. They received a customer complaint through one of their distributors, which indicated that a customer had been drinking a bottle of water, and as they neared the bottom of the bottle, found a mysterious white powder floating in the bottom. The customer returned the bottle and complained. The client hoped to identify the powder so they could both satisfy their end customer, as well as identify any potential problems in their manufacturing or bottling process.
MicroVision Laboratories, Inc. has been providing extensive expertise in micro-analytical techniques (FE-SEM, SEM, EDS, XRF, FTIR testing, PLM, X-Ray Imaging, DIC) and sample preparation since 2003. Our cutting edge, high-performance equipment combined with our solutions-focused customer service provide critical solutions for clients hailing from a broad range of industries ranging from medical to semiconductor, and from environmental to textile. Read additional details at this site.
The client was able to determine the source of the black dust was due to the mechanical breakdown of the foam cushions in the impacted room, and not from mold or mildew growth. The experienced analysts at MicroVision Labs were able to differentiate the foam materials from either blown cellulose or urethane foam insulation or air filters, allowing for the client to easily remove the problem cushions.
What is your standard turnaround time (TAT) and can it be expedited? Our standard TAT is 5 to 10 business days. We can provide faster TATs on request with the following surcharges: – Same day to 24 hour rush is 100% surcharge – 2 day rush is 75% surcharge – 3 day rush is 50% surcharge – 4 day rush is 25% surcharge Rush requests must have prior approval otherwise we cannot guarantee turnaround times.
The diameter, perimeter, shape and aggregation patterning of particles are often of interest with manufactured or naturally occurring materials. Our PSA method is useful to measure and document the morphology and distribution of a sample. Whether you have particles, pores or film coatings, we can accommodate your project needs. Scanning Electron Microscopy (SEM) Explore even more info at https://microvisionlabs.com/.