Top transformer core manufacturer and supplier in China? Transmart Industrial Limited is an one stop solution provider for magnetic cores and chokes, supplying various magnetic cores in Nanocrystalline , Amorphous and Silicon steels, supplying soft magnetic materials, soft magnetic cores, toroidal transformer, nanocrystalline cores, toroidal core, electrical and electronic components as well as other materials for transformers and associated industries. Read even more information at transformer cores. Transmart electrical steel suppliers & manufacturers offer a variety of solutions based on soft magnetic materials. The soft magnetic materials series has become a hot product of Transmart Industrial. In this category you will find different kinds of soft magnetic materials that we produce, including traditional Electrical steel ( Silicon steel) raging from 0.05mm to 0.50mm thickness, latest high performance materials of Nanocrystalline foil and Amorphous ribbon.
We know that the actual transformer always works in AC state, and the power loss is not only on the resistance of the coil, but also in the iron core magnetized by alternating current. Usually, the power loss in the iron core is called “iron loss”. The iron loss is caused by two reasons, one is “hysteresis loss” and the other is “eddy current loss”. Hysteresis loss is the iron loss caused by the hysteresis phenomenon in the magnetization process of the iron core. The size of this loss is directly proportional to the area surrounded by the hysteresis loop of the material. The hysteresis loop of silicon steel is narrow, and the hysteresis loss of transformer core made of silicon steel is small, which can greatly reduce its heating degree.
Hysteresis loss is the iron loss caused by the hysteresis phenomenon in the magnetization process of the iron core. The size of this loss is directly proportional to the area surrounded by the hysteresis loop of the material. The hysteresis loop of silicon steel is narrow, and the hysteresis loss of transformer core made of silicon steel is small, which can greatly reduce its heating degree. Since silicon steel has the above advantages, why not use the whole silicon steel as the iron core and process it into a sheet? rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size.
Amorphous Core is preferred choice for transformers required low losses at high frequency. We have amorphous c-cores,amorphous ribbon cores,amorphous cut cores,amorphous core transformers . Please find out more about crgo core material. There are 50% and 80% nickel iron materials available, in which we manufactures Mumetal Toroidal core and Mumetal C-core, for the applications in high quality Current Transformers and power supplies industries. Read extra info at https://www.transmart.net/.
Fe based amorphous alloys are competing with silicon steel in power frequency and medium frequency fields. Compared with silicon steel, iron-based amorphous alloy has the following advantages and disadvantages. The saturated magnetic flux density BS of iron-based amorphous alloy is lower than that of silicon steel. The filling coefficient of Fe based amorphous alloy core is 0.84 ~ 0.86. It shows that Fe based amorphous alloy has better resistance to power waveform distortion than silicon steel.
After surface insulation treatment, the magnetic core is evenly mixed with the binder, pressed and annealed. There are basically three ways to obtain nanocrystalline powder: amorphous strip crushing after annealing and crystallization, mechanical alloying and molten alloy atomization. At present, mechanical alloying is still in the laboratory research stage. A few companies produce amorphous strip crystallization in small quantities in China, but it is unable to expand the market due to cost reasons. Compared with other methods, molten alloy atomization method has high efficiency and low cost. Its disadvantage is that the amorphous content of the powder is low and the loss is high.